High-Quality POM Rod for Precision Engineering and Fabrication Needs

• Customization: Available
• Material: POM
• Kind: Plastic Bar
• Model NO.: POM ROD
• Water Absorption: 0.2%~0.3%
• Contraction Percentage: 1.5%-2.2%
• Tensile Strength: 55-65MPa
• Flexural Strength: 90 - 95 MPa
• Hardness: 80 - 85 Shore D
• Density: 1.42 G/Cm³
• Heat Deflection Temperature: 165℃ (0.45 MPa)
• Transport Package: Wooden Box
• Specification: Customizable
• Trademark: Hansa
• Origin: Jiangsu China
• Production Capacity: 20t/Month
• Package Size: 102.00cm * 15.00cm * 15.00cm
• Package Gross Weight: 1.110kg

Product Description

Product Description

Type	Size(mm)	Color:natural color and black
Sheet	1000*2000 Thickness:8-10	Color:natural color and black
ESD Sheet	Color:naturalThickness:8-40	615*1230
	Color:black Thickness:8-50
Rod	Diameter:θ4-θ200 Test	Color:natural color or black

Project			Test method	Unit	Typical value
					PCM-H	PCM-C	PCM-SO
Basic performance	Density		IS0 1183	g/cm³	1.43	1.41	1.33
	Bibulous rate		IS0 62	%	0.23	0.22	0.2
	Tensile modulus		IS0 527	Mpa	3600 78	2900 64	—
Mechanical properties	Yield stress		IS0 527	Mpa	35	35	—
	Yield strain		IS0 527	%	100	90	—
	Flexural strength		IS0 178	Mpa	2800	2800	50
	Pendulum impact strength		IS0 179	Kj/m²	200	150	—
	Pendulum impact strength		IS0 179	Kj/m²	10	7.0	—
Thermal performance	Melting point		IS0 8146	℃	175	166	166
	Loaddeflection temperature	(1.80Mpa)	IS0 8146	℃	175 170	105 156	— —
		(0.45Mpa)
	Thermal deforma- tiontemperature	18.6kgt/cm²	D648	℃	—	—	100 140
		4.6kgt/cm²
Electrical	Dielectric constant	(100HZ)	IEC 250	—	3.9	3.9	—

Material Introduction

Polyoxymethylene (POM),  is a high-performance engineering plastic celebrated for its exceptional mechanical integrity, dimensional stability, and versatility in precision applications. Characterized by a linear molecular structure of repeating oxymethylene units, POM bridges the gap between traditional plastics and metals, offering a unique blend of rigidity, toughness, and wear resistance that makes it indispensable across industrial, automotive, and consumer sectors. Unlike many polymers, it maintains consistent performance across a wide temperature range (-40°C to 100°C for continuous use) and exhibits minimal creep under sustained load, ensuring reliability in critical components.
Its mechanical properties stand out among engineering plastics: POM delivers a tensile strength of 60–85 MPa, flexural modulus of 2.5–3.8 GPa, and impact strength (notched Izod) of 6–12 kJ/m², balancing rigidity with ductility for applications requiring both load-bearing capacity and resistance to sudden shocks. A key advantage is its excellent dimensional accuracy—with a low coefficient of linear thermal expansion  and near-zero moisture absorption ( at saturation), POM retains tight tolerances even in humid or temperature-fluctuating environments, eliminating the need for post-processing adjustments. Additionally, its low coefficient of friction (0.15–0.30, dry) and self-lubricating properties make it ideal for moving parts, reducing friction-induced wear and extending service life without frequent lubrication.
Chemically resilient, POM resists attack from fuels, oils, greases, and most organic solvents, while withstanding mild acids and alkalis—making it suitable for harsh operating conditions in automotive and industrial systems. It also boasts good machinability, allowing for precise turning, milling, and injection molding into complex geometries, from small gears to large structural components. Unlike some engineering plastics, POM requires no reinforcing fillers to achieve its core performance, though glass-fiber or carbon-fiber reinforced grades are available for enhanced stiffness in high-load applications
Key applications span diverse industries: